WI POWER 75

  1. Home
  2. Products
  3. Weld-inn Welding Consumables
  4. Weld-inn Welding Electrodes
  5. Weld-inn Low Alloyed High Strength Electrodes
  6. WI POWER 75
Brand Weld-inn
Product WI POWER 75
Datasheet
Standards
EN ISO 18275-A E 62 6 Z 1NiMo B 4 2 H5
AWS A5.5 E 10018 - G H4
Chemical Composition of Weld Metal % (Typical)
C Mn Si Ni Cr Mo
0.05 1.3 0.5 1.3 0.3 0.5
Typical Base Material Grades
  • The yield strength of 620 N/mm2 up to the quenched and tempered fine grain steels
  • The tensile strength of the 780 N/mm2 heat treating steels.
Mechanical Properties
Yield Strength (N/mm²) Tensile Strength (N/mm²) Heat Treatment Impact Strength (ISO-V/-60°C) Elongation ((Lo=5do) (%))
min.620 690-890 560-600°C/ 1 h/ 300°C (air) min.47 J min.18
Features and Applications
  • Content of Mn-Mo-Ni alloy
  • High ductility and high resistance to cracking obtained in welding high-strength, quenched and tempered, fine-grained structural steels
  • Suitability for use in welding of materials with service temperatures between -60°C and +400°C
  • Very high values of impact resistance after aging
  • Convenience of welding at all positions except for the vertical down position.
  • Possibility of applying same heat treatment temperatures at pre- and post-welding as well as at transition stagesas those of base metal
  • Weld deposits with very low contents of hydrogen
  • Requirement of re-drying for minimum 2 hours at the temperatures between 300°C and 350°C
Current Type
  • D.C.(+)
Welding Positions
Operating Data
Product code Diameter x Length (inch) Welding Current (A) Weight g / 100 pcs Diameter x Length (mm)
2010800153 3/32 x 14” 80 - 110 2280 2.50 x 350
2010800154 1/8 x 14” 100-140 3580 3.20 x 350
2010800155 5/32 x 18” 130 - 190 6680 4.00 x 450
2010800156 3/16 x 18” 190 - 240 10230 5.00 x 450