Brand Weld-inn
Product WI MS
Datasheet
Standards
EN IS014174 SA CS/MS 1 68 AC
AWS A5.17 F6AO-EM12 / F6AZ-EL12
Chemical Composition of Weld Metal % (Typical)
Basicity
1.0
Mechanical Properties (Typical)
SAW Wire AWS A5.17/ AWS A5.23 Yield Strength (N/mm2) Tensile Strength (N/mm2) Elongation ((Lo=5do) (%) lmpact Strength IS0-V(J) -0°C lmpact Strength IS0-V(J) -20°C
WI S1 F6AZ-EL12 395 475 24 38 ---
WI S2 F6AO-EM12 390 485 30 --- 69
Features and Applications
  • A type of SAW flux structured from agglomerated manganese silicate and calcium silicate
  • Basicity of the flux according to Boniszewski formula is 1,0
  • Weld beads of excellent surface appearance and with easily removed slags
  • High resistance to porosity caused by oil and rust
  • High capacity of current flow
  • Suitability for use in 2-pass welding operations on thick materials (best choice for base metals in thicknesses of 10-40 mm)
  • Requirement of re-drying at 250-350°C for 2 hours
Chemical Compositon of Weld Metal - % ( Typical)
SAW Wire C Si Mn
WI S1 0.05 0.80 1.10
WI S2 0.04 0.45 1.27
Operating Data
Product code Package Weight (Kg) Package Type
2010700008 25 Kraft Bag