WI HFE 600 S

  1. Home
  2. Products
  3. Weld-inn Welding Consumables
  4. Weld-inn Welding Electrodes
  5. Weld-inn Hardfacing Electrodes
  6. WI HFE 600 S
Brand Weld-inn
Product WI HFE 600 S
Datasheet
Standards
EN 14700 E Fe 8
DIN 8555 E6-UM-60 P
Chemical Composition of Weld Metal % (Typical)
C Cr Si
0.5 9.0 1.8
Features and Applications
  • Applicability in final-layer hardfacing of parts of earth and mineral mining machines, impact drilling and crushing devices, guide springs, edges of cutting tools, hard manganese steels, bucket edges and teeth, all of which are made of alloyed or unalloyed steels, as well as in other materials required to have high resistance to wear
  • Electrode of basic type with thick coating
  • lnclusion of chromium-silicon alloy, very hard electrode
  • Weld metal with ductile and cracking-resistant behaviors
  • Crack resistance to impact forcing due to its high ductility
  • Machinability of weld metal through grinding only
  • Requirement of re-drying at 300°C for 2 hours for moistened electrodes
  • Recommended pre-heating at 200-300°C for welding thick work pieces and materials tending to get hardene
  • Requirement of 2-3 layers hardfacing to obtain the highest resistance to wear
Mechanical Properties
Weld Metal Hardness (HRC) Soft Annealing Hardening Tempered
54 - 58 780- 820°C Slow Cooling in Furnace 1000 - 1050°C in oil 300-400°C
Current Type
  • D.C.(+)
Welding Positions
Operating Data
Product code Welding Current (A) Weight g / 100 pcs Diameter x Length (mm) Diameter x Length (inch)
2010800035 100-140 3650 3.20 x 350 1/8 x 14”
2010800036 140-180 6840 4.00 x 450 5/32 x 18”
2010800037 180-230 10900 5.00 x 450 3/16 x 18”